Product Line
Home > Product Line > Polymer Materials > RESINS FOR PAINTS
RESINS FOR PAINTS
Description
●Universal Color Tint Resin
●Interior Auto Parts
●Helmet(ABS)
●Car Bumper
●Coil Coating
●SMP Resin for Non Stick Pot Coating
●White Can Coating
●Concrete Paints(Road Mark)
●Coating for Zinc Galvanizes Metal
●Plastic Coating
●Wheel Rims Coating
●Bicycles' Frame Coating
●Wood Coating
●Helmet(ABS)
●Car Bumper
●Coil Coating
●SMP Resin for Non Stick Pot Coating
●White Can Coating
●Concrete Paints(Road Mark)
●Coating for Zinc Galvanizes Metal
●Plastic Coating
●Wheel Rims Coating
●Bicycles' Frame Coating
●Wood Coating
| Product Grade | Characteristic | Application |
| AC-5030 (Primer) |
Fast drying,Hardness | Lacquer and Acrylic Polyol for Plastic |
| AC-5060 (Primer) |
Fast drying,Hardness,Good Aluminum Orientation | |
| AC-5052 (Primer) |
Low OH value,Fast Drying good compatibility with CAB and good Aluminum orientation |
PU primer for auto-refinish |
| AC-5066 (Primer/Metallic BASE) |
Fast drying,Excellent compatibility, Yellowing resistance |
Acrylic Polyol for 3C and Auto Refinish |
| AC-5080 (Clear/Base Coat) |
Excellent weather resistance, Fast curing, Well hardness, Yellowing resistancce |
Polyurethane paints for general purpose, For ABS, automobile repairing |
| AC-5080X (Clear/Base Coat) |
Excellent weather resistance, Fast curing, Well hardness, Yellowing resistancce |
Economically PU paints for general purpose, For ABS, automobile repairing |
| AC-5090 (Clear/Base Coat) |
Ultra fast drying, Excellent resistance, Good Hardness, Aromatic Solvent free |
Polyurethane paints for High end purpose |
| AC-5091 (Clear/Base Coat) |
Ultra fast drying, Excellent resistance, Good Hardness, Aromatic Solvent free, Yellowing Resistance |
|
| AC-5180 (Clear/Base Coat) |
Fast dry, Chemical resistance | Coating for Metal and Wood |
| AC-5181 (Clear/Base Coat) |
Fast drying, Good Hardness, Economy type PU for top coat and base coat |
Polyurethane paints for general purpose |
| AC-5107 (Clear Coat) |
Excellent weather resistance, High Film Build, Good adhesion |
Advance PU for top Coat |
| AC-5680 (Clear Coat) |
High Solid Low Viscosity, Good waether resistance, Good Hardness |
|
| AC-5101 (Clear Coat) |
Gloss, Flexible, Weather resistance | Top Coat for General purpose |
| AC-5105 (Clear Coat) |
High solid and low viscosity, High hardness, High Film Build |
Advance PU for Top Coat |
| AC-5131 (Clear Coat) |
High solid and low viscosity, High hardness, High Film Build |
|
| AC-5140 (Clear Coat) |
High solid and low viscosity, High hardness, Aromatic solvent free |
|
| AC-5106 (Clear Coat) |
High Film Build, good gloss, good adhesion | Economically top coat for Auto Refinish |
| AC-5502 (Clear Coat) |
High Gloss, Good adhesion, Hardness | |
| AC-5500 (Clear Coat) |
High gloss, Pigment dispersibility, Hardness, Easy to daub |
Coating for Metal, Plastic and Wood |
| A1229-70X (Primer/Binder) |
Good Flexibility, Good adhesion, Hardness, Good weather resistance |
Coating for auto refinish as primer or base coat |
◎specification
| Product Grade | Solid Content (%) |
Viscosity 25℃ (Gardner) |
OH Value (Supplied) |
OH Content %(solid) |
Acid Value (Solid) |
Solvent |
| AC-5030 (Primer) |
55.0±1.0 | Y~Z2 | 16.5 | 0.9 | ≦8 | Toluene/BAC |
| AC-5060 (Primer) |
55.0±1.0 | Y~Z2 | 33 | 1.8 | ≦8 | Toluene/BAC |
| AC-5052 (Primer) |
53.0±1.0 | Z2~Z5 | 25 | 1.5 | ≦6 | Toluene/BAC |
| AC-5066 (Primer/Metallic BASE) |
50.0±1.0 | Z~Z3 | 33 | 2 | ≦6 | Toluene/BAC |
| AC-5080 (Clear/Base Coat) |
60.0±1.0 | Z2~Z5 | 48 | 2.4 | ≦10 | Xylene/PMA |
| AC-5080X (Clear/Base Coat) |
61.0±1.0 | Z1~Z3 | 48 | 2.4 | ≦10 | Xylene |
| AC-5090 (Clear/Base Coat) |
60.0±1.0 | W~Z1 | 54 | 2.7 | ≦14 | BAC/MEK |
| AC-5091 (Clear/Base Coat) |
60.0±1.0 | Z3~Z6 | 54 | 2.7 | ≦14 | BAC/MEK |
| AC-5180 (Clear/Base Coat) |
60.0±1.0 | Z2~Z5 | 48 | 2.4 | ≦8 | Xylene |
| AC-5181 (Clear/Base Coat) |
61.0±1.0 | Z1~Z4 | 48 | 2.4 | ≦6 | Xylene/BAC |
| AC-5107 (Clear Coat) |
65.0±1.0 | Z1~Z5 | 65 | 3 | ≦9 | Xylene/PMA |
| AC-5680 (Clear Coat) |
70.0±2.0 | Z~Z3 | 56 | 2.4 | ≦10 | Xylene/PMA |
| AC-5101 (Clear Coat) |
70.0±1.0 | Z4~Z7 | 70 | 3 | ≦10 | Xylene/PMA /DBE |
| AC-5105 (Clear Coat) |
70.0±2.0 | Z1~Z4 | 70 | 3 | ≦6 | BAC/Xylene |
| AC-5131 (Clear Coat) |
70.0±1.0 | Z1~Z5 | 84.7 | 3.7 | ≦10 | BAC/Xylene |
| AC-5140 (Clear Coat) |
70.0±2.0 | Z2~Z5 | 98 | 4.2 | ≦14 | BAC |
| AC-5106 (Clear Coat) |
70.0±2.0 | Z3~Z6 | 70 | 3 | ≦11 | Xylene/BAC |
| AC-5502 (Clear Coat) |
65.0±1.0 | Z1~Z5 | 85 | 4 | ≦11 | Xylene/PMA |
| AC-5500 (Clear Coat) |
60.0±1.0 | X~Z1 | 79 | 4 | ≦10 | Xylene/PMA |
| A1229-70X (Primer/Binder) |
70.0±1.0 | Y~Z3 | 48.3 | 2.09 | ≦7 | Xylene |
| Product Grade | Characteristic | Application |
| DCP-651 | Excellent pigment dispersion, Good compatibility to various resin, High Tg, Contains of OH functional group |
Gringing binder for high concentration color paste, suitable for Varnish and Tinting base |
◎specification
| Product Grade | Solid Content (%) |
Viscosity 25℃ (Gardner) |
OH Value (Supplied) |
OH Content %(solid) |
Acid Value (Solid) |
Solvent |
| DCP-651 | 60.0±2.0 | V~Z | 30 | 1.5 | ≦2 | Xylene/PMA |
| Product Grade | Characteristic | Application |
| AC-5066 (Primer/Base Coat) |
Fast drying,Excellent compatibility, Yellowing resistance |
Acrylic Polyol for 3C and Auto Refinish |
| AC-5140 (Clear Coat) |
High solid and Low viscosity, High hardness, Aromatic solvent free |
Advance PU for Top Coat |
◎specification
| Product Grade | Solid Content (%) |
Viscosity 25℃ (Gardner) |
OH Value (Supplied) |
OH Content %(solid) |
Acid Value (Solid) |
Solvent |
| AC-5066 (Primer/Base Coat) |
50.0±1.0 | Z~Z3 | 33 | 2 | ≦6 | Toluene/BAC |
| AC-5140 (Clear Coat) |
70.0±2.0 | Z2~Z5 | 98 | 4.2 | ≦14 | BAC |
| Product Grade | Characteristic | Application |
| AC-5066 (Primer/Base Coat) |
Fast drying,Excellent compatibility, Yellowing resistance |
Acrylic Polyol for 3C and Auto Refinish |
| AC-5500 (Clear Coat) |
High gloss, Pigment dispersibility, Hardness, Easy to daub |
Coating for Metal, Plastic and Wood, Powder coating refinishing |
| AC-5140 (Clear Coat) |
High solid and Low viscosity, High hardness, Aromatic solvent free |
Advance PU for Top Coat |
◎specification
| Product Grade | Solid Content (%) |
Viscosity 25℃ (Gardner) |
OH Value (Supplied) |
OH Content %(solid) |
Acid Value (Solid) |
Solvent |
| AC-5066 (Primer/Base Coat) |
50.0±1.0 | Z~Z3 | 33 | 2 | ≦6 | Toluene/BAC |
| AC-5500 (Clear Coat) |
60.0±1.0 | X~Z1 | 79 | 4 | ≦10 | Xylene/PMA |
| AC-5140 (Clear Coat) |
70.0±2.0 | Z2~Z5 | 98 | 4.2 | ≦14 | BAC |
| Product Grade | Characteristic | Application |
| AC-5700 | High OHV,Low Viscosity | Paints for Automotive refinish and Car Bumper |
| AC-5151 | High OHV,Low Viscosity |
◎specification
| Product Grade | Solid Content (%) |
Viscosity 25℃ (Gardner) |
OH Value (Supplied) |
OH Content %(solid) |
Acid Value (Solid) |
Solvent |
| AC-5700 | 50.0~51.0 | F~I | 85 | 5.2 | ≦9 | - |
| AC-5151 | 50.0±1.0 | C~DE | 75 | 4.5 | ≦7 | - |
| Product Grade | Characteristic | Application |
| AC-1103-50 (Primer) |
Leveling,Adhesion,Excellent Chemical resistance, good in Acid/Alkali Resistance |
For PCM Baking |
| A1222-60 (Back Coat) |
Toughness, Hardness, Adhesion, Processability | |
| A1229-70 (Front Coat) |
Weather Resistance, Flexible, Hardness, Toughess | |
| A1233-70 (Front Coat) |
Toughness,Hardness, Weather&Yellowing Resistance | |
| A18330-60 (Front Coat) |
Silicone Modified Polymer resin. Hardness. Good in Heat-resistance, fortemperature up to 300℃, MEK Resistance, Adhesion |
◎specification
| Product Grade | Solid Content (%) |
Viscosity 25℃ (Gardner) |
OH Value (Supplied) |
OH Content %(solid) |
Acid Value (Solid) |
Solvent |
| A1103-50 (Primer) |
50.0±1.0 | Y~Z2 | - | - | ≦0.5 | Solvesso 150/BCS |
| A1222-60 (Back Coat) |
60.0±1.0 | U~X | - | - | ≦8 | Solvesso 153/Xylene |
| A1229-70 (Front Coat) |
70.0±1.0 | Z4~Z6 | - | - | ≦8 | Solvesso 153/Xylene |
| A1233-70 (Front Coat) |
70.0±1.0 | X~Z1 | - | - | ≦10 | Solvesso 153/Xylene |
| A18330-60 (Front Coat) |
60 | ≒W | - | - | ≦10 | PMA/DMAC |
| Product Grade | Characteristic | Application |
| A18310-60A | Slilcone Modified Polymer resin. Hardness. General purpose in Heat-resistance, for temperature up to 300℃, MEK Resistance, Adhesion |
For heat resistance coating, especially apply on non stick pot |
| A18330-60 | Silicone Modified Polymer resin. Hardness. Good in heat-resistance, for temperature up to 300℃, MEK Resistance, Adhesion |
|
| A18350-60A | Silicone Modidied Polymer resin. Hardness. Excellent Heat-resistance, for temperature up to 300℃, MEK Resistance, Adhesion |
◎specification
| Product Grade | Solid Content (%) |
Viscosity 25℃ (Gardner) |
OH Value (Supplied) |
OH Content %(solid) |
Acid Value (Solid) |
Solvent |
| A18310-60A | 60 | W~Z1 | - | - | ≦10 | PMA |
| A18330-60 | 60 | U~Y | - | - | ≦10 | PMA |
| A18350-60A | 60 | S~W | - | - | ≦10 | PMA |
| Product Grade | Characteristic | Application |
| A1212-60 | Hardness, Adhesion, Impact and Processability |
For white can coating and advance baking enamel |
| A1226-70 | Gloss, Adhesionm Bending & Impact Resistance |
For white can coating and advance baking enamel, PU Coating |
◎specification
| Product Grade | Solid Content (%) |
Viscosity 25℃ (Gardner) |
OH Value (Supplied) |
OH Content %(solid) |
Acid Value (Solid) |
Solvent |
| A1212-60 | 60±1.0 | YZ~Z2 | - | - | ≦9 | Solvesso 153/BAC |
| A18330-60 | 70 | Z~Z3 | - | - | ≦10 | Xylene/BAC |
| Product Grade | Characteristic | Application |
| AC-1000C | Excellent Alkali Resistance, Gloss, Precessability |
For Concrete Paint |
| AC-1000AN | Gloss, Alkali Resistance | |
| AC-1003 | Good durability, Good resistance to Yellowingm Fast drying |
|
| AC-1100 | Low Viscosity, Gloss, Alkali Resistance | |
| AC-1600 | Weather Resistance, Alkali Resistance |
◎specification
| Product Grade | Solid Content (%) |
Viscosity 25℃ (Gardner) |
Glass Transition Temperature |
OH Content %(solid) |
Acid Value (Solid) |
Solvent |
| AC-1000C | 50.0±1.5 | Y~Z2 | Tg=53℃ | - | ≦9 | Xylene |
| AC-1000AN | 54.0±2.0 | Z3~Z6 | Tg=57℃ | - | ≦8 | Toluene/ Xylene/ N-BAC |
| AC-1003 | 60.0±2.0 | Z3~Z6 | TG=14℃ | - | ≦8 | Toluene |
| AC-1100 | 50.0±1.0 | X~Z1 | Tg=53℃ | - | ≦9 | Solvesso100/ Toluene/ VM&P Naphtha |
| AC-1600 | 50.0±1.0 | Z3~Z6 | TG=43℃ | - | ≦3 | Solvesso100 |
| Product Grade | Characteristic | Application |
| AC-1202 | Good adhesion, Flexibility, Gloss | Paint for Zinc Galvanized metal Powder coating refinishing |
◎specification
| Product Grade | Solid Content (%) |
Viscosity 25℃ (Gardner) |
Glass Transition Temperature |
OH Content %(solid) |
Acid Value (Solid) |
Solvent |
| AC-1202 | 60±1.0 | Z5~Z7 | Tg=35℃ | 0.75 | ≦25 | Xylene/ N-BAC/ Toluene |
| Product Grade | Characteristic | Application |
| AC-3403 | Excellent comapibility with NC & CAB, Hardness, Abrasion, Alcohol Resistance |
Lacquer For Plastic |
| AC-3406 | Excellent comaptibility with NC & CAB, Gloss, Pigment Dispersibility |
|
| AC-3700 | Hardness, Adhesion, Yellowing Resistance, Fast Drying, Compatible with CAB |
Laquer for metal, Plastic and wood. Also as PU lacquer |
| AC-3000AK | Adhesion, Toughness, Dispersibility, Compatible with NC |
Lacquer for metal, Plastic and wood |
| AC-3095 | Hardness, Adhesion, Fast Drying, Compatible with NC |
◎specification
| Product Grade | Solid Content (%) |
Viscosity 25℃ (Gardner) |
Glass Transition Temperature |
OH Content %(solid) |
Acid Value (Solid) |
Solvent |
| AC-3403 | 50±1.0 | X~Z1 | Tg=65℃ | - | ≦4 | Toluene/ i-Butanol |
| AC-3406 | 50.0±1.0 | X~Z1 | Tg=48℃ | - | ≦6 | Toluene/ Xylene/ i-Butanol |
| AC-3700 | 50.0±1.0 | X~Z1 | Tg=54℃ | 1.2 | ≦7 | Toluene |
| AC-3000AK | 50.0±1.0 | Y~Z2 | Tg=50℃ | - | ≦1 | Toluene/ Xylene/ n-Butanol |
| AC-3095 | 63.0±1.0 | Z3~Z6 | Tg=95℃ | 2 | ≦9 | Xylene- N-BAC/ acetat |
| Product Grade | Characteristic | Application |
| AC-4600 | Impact resistance, 2nd Physical properties, Pigment dispersibility |
Baking enamel for home appliance and general purpose |
| AC-4610 | High solid, Physical properties, Toughness |
◎specification
| Product Grade | Solid Content (%) |
Viscosity 25℃ (Gardner) |
OH Value (Supplied) |
OH Content %(solid) |
Acid Value (Solid) |
Solvent |
| AC-4600 | 60±1.0 | X~Z1 | - | - | ≦8 | Xylene/ i-Butanol/ PMA |
| AC-4610 | 70±1.0 | Z1~Z3 | - | - | ≦7 | Xylene/PMA |
| Product Grade | Characteristic | Application |
| AC-4610 (top Coat) |
High solid, Physical properties, Toughness | Baking enamel general purpose |
| A136-70 | Gloss, Impact Resistance, Adhesion | For baking paints, lacquer, PU paints, acid cured Amino-Alkyd paints |
| A136-70H | Gloss, Adhesion, Impact Resistance, High viscosity |
|
| A139-70 | Gloss, Adhesion, Impact Resistance,storage | |
| A436-70 | Light color, Hardness, Yellowing resistance, Gloss |
Advance Baking Paints |
◎specification
| Product Grade | Solid Content (%) |
Viscosity 25℃ (Gardner) |
Oil Type | Oil Length | Acid Value (Solid) |
Solvent |
| AC-4610 (Top Coat) |
70±1.0 | Z1~Z3 | - | - | ≦7 | Xylene/PMA |
| A136-70 | 70.0±1.0 | Z~Z3(60%) | Oil type=Soya | Oil length=34% | ≦6 | Xylene |
| A136-70H | 70.0±1.0 | Z2~Z4(60%) | Oil type=Soya | Oil length=34% | ≦6 | Xylene |
| A139-70 | 70.0±1.0 | Z~Z3(60%) | Oil type=Soya | Oil length=34% | ≦6 | Xylene |
| A436-70 | 70.0±1.0 | Z~Z3(60%) | Oil type=Coconut/ Palm kernel |
Oil length=34% | ≦10 | Xylene |
| Product Grade | Characteristic | Application |
| A136-70 | Gloss, Impact Resistance, Adhesion | For baking paints, lacquer, PU paints, acid cured Amino-Alkyd paints |
| A136-70H | Gloss, Adhesion, Impact Resistance, High viscosity |
|
| A139-70 | Gloss, Adhesion, Impact Resistance,storage | |
| A432-70 | Light color, Hardness, Yellowing resistance, Semi Gloss |
For lacquer, PU paints, acid-cured Amino-Alkyd paints |
| A421-70 | Low OH value, Fast drying, Easy to sand, Semi gloss |
For lacquer, PU paints |
| A931-70 | Light color, Hardness, Weather resistance | |
| A931-60 | Flexibility, Gloss, Impact resistance, Bending | |
| A633-95 (Blow Castor Oil) |
Gloss, Flexibility, Impact resistance | |
| A431-80 | Low viscosity, Gloss, High film build | For PU paints |
| A931-80 | Light color, Hardness, Adhesion, Chemical resistance |
|
| A210-95 | Drying Wipping, Tinting strengh, Low viscosity |
Stain for wood(Glaze) |
| A211-100 | Drting, Color dispersibility, Wipping, Low viscosity |
◎specification
| Product Grade | Solid Content (%) |
Viscosity 25℃ (Gardner) |
Oil Type | Oil Length | Acid Value (Solid) |
Solvent |
| A136-70 | 70.0±1.0 | Z~Z3(60%) | Oil type=Soya | Oil length=34% | ≦6 | Xylene |
| A136-70H | 70.0±1.0 | Z4~Z6(60%) | Oil type=Soya | Oil length=34% | ≦6 | Xylene |
| A139-70 | 70.0±1.0 | Z~Z3(60%) | Oil type=Soya | Oil length=34% | ≦6 | Xylene |
| A432-70 | 70.0±1.0 | Y~Z3(60%) | Oil type=Coconut/ Palm kernel |
Oil length=34% | ≦10 | Xylene |
| A421-70 | 70 | X~Z1(60%) | Oil type=Coconut/ Palm kernel |
Oil length=51% | ≦9 | Xylene |
| A931-70 | 70.0±1.0 | Y~Z2(60%) | synthetic Fatty Acid |
Oil length=38% | ≦10 | Xylene |
| A631-60 | 60.0±1.0 | V~Y(60%) | Oil type=Castor | Oil length=44% | ≦15 | Xylene |
| A633-95 (Blow Castor Oil) |
95.0±1.0 | P~T(95%) | Oil type=Castor | - | ≦1 | Xylene |
| A431-80 | 80.0±1.0 | X~Z1(70%) | Oil type=Coconut/ Palm kernel |
Oil length=33% | ≦8 | Xylene/BAC |
| A931-80 | 80.0±1.0 | P~T(60%) | synthetic Fatty Acid |
Oil length=39% | ≦10 | Xylene |
| A210-95 | 95.0±1.0 | J~O(95%) | Oil type=Linseed | Oil length=78% | ≦4 | Xylene |
| A211-100 | ≧99.0 | A~C(95%) | Oil type=Linseed | Oil length=100% | ≦2.5 | - |